Relaxed with Orb v3; 0.03 eV/Å threshold; final energy = -41.5525 eV; energy change = -7.9131 eV; symmetry: P4mm → P1
Fe2CoMnAlN (space group: P4mm #99, crystal system: tetragonal, point group: 4mm) (missed expected composition: Fe2CoMnAlN)
Phase diagram of MnAlFe2CoN; e_above_hull: 1.106997 eV/atom; predicted_stable: False