Relaxed with Orb v3; 0.03 eV/Å threshold; final energy = -30.8458 eV; energy change = -38.5475 eV; symmetry: P4mm → P4mm
Fe2MnNiAl (space group: P4mm #99, crystal system: tetragonal, point group: 4mm)
Phase diagram of MnAlFe2Ni; e_above_hull: 1.190918 eV/atom; predicted_stable: False